Considerations for proper selection of dental cements
James F Simon1, Laura A Darnell
1Division of Esthetic Dentistry, Department of Restorative Dentistry, University of Tennessee College of Dentistry, Memphis, Tennessee, USA.
Compendium of Continuing Education in Dentistry (Jamesburg, N.J. : 1995)
|March 22, 2012
Summary
Choosing the right dental cement is crucial for indirect restoration success. Proper cement selection ensures adequate bond strength and retention, impacting the longevity of dental work.
Area of Science:
- Dental Materials Science
- Restorative Dentistry
Background:
- The increasing variety of materials for indirect restorations complicates dental cement selection.
- Proper cement choice is vital for the success of dental restorations.
Purpose of the Study:
- To highlight the importance of selecting appropriate dental cements for indirect restorations.
- To underscore the role of cement in achieving sufficient bond strength and retention.
Main Methods:
- Literature review on dental cements and indirect restorations.
- Analysis of cement functions including sealing and retention support.
Main Results:
- Cement selection significantly impacts restoration bond strength.
- Different cements offer varying degrees of retention support for restorations.
Conclusions:
- Careful consideration of cement properties is essential prior to selection.
- Optimal cement choice is a key factor in ensuring the functional success and durability of indirect restorations.
Related Concept Videos
01:22Types of Cement II
Portland blast-furnace cement is made by blending Portland cement clinker with granulated blast-furnace slag, which accounts for 25 to 65 percent of the cement's weight. Despite its similarities to ordinary Portland (Type I) cement in terms of fineness and setting times, its early strength is lower, though it achieves comparable strength later on. It's particularly suited for mass concrete structures and marine environments due to its lower heat of hydration and superior sulfate resistance.
01:17Soundness of Cement
The soundness of cement refers to the ability of cement paste to retain its volume after setting. Unsound cement can lead to expansion and structural damage due to the presence of free lime, magnesia, and calcium sulfate. Free lime hydrates very slowly, expanding and causing unsoundness, which is difficult to detect because it intercrystallizes with other compounds. Magnesia also reacts with water, forming crystals that can disrupt the cement's structure. Calcium sulfate can create ettringite,...
01:21Types of Cement I
Portland cement comes in several types, each with distinct properties and applications based on their chemical composition and hydration characteristics:
Type I (Ordinary Portland Cement) is widely used for general construction where special properties are not required. It has moderate sulfate resistance and heat of hydration.
Type II (Modified Cement) offers moderate resistance to sulfate attack and a lower rate of heat development compared to Type I. It is suitable for structures in...
Type I (Ordinary Portland Cement) is widely used for general construction where special properties are not required. It has moderate sulfate resistance and heat of hydration.
Type II (Modified Cement) offers moderate resistance to sulfate attack and a lower rate of heat development compared to Type I. It is suitable for structures in...
01:17Mortar Properties
Mortar properties encompass a range of characteristics crucial for construction and masonry work, including workability, water retention, bond strength, durability, compressive strength, volume change, and appearance. Workability refers to mortar's ability to be easily applied and manipulated without sagging or falling off surfaces, which is important for efficient masonry unit placement and alignment. Water retention is essential to prevent the mortar from losing moisture too quickly to the...
01:20Strength of Cement
Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
01:15Fineness of Cement
The fineness of cement directly influences the rate of hydration, as the hydration begins at the surface of the cement particles. In addition to hydration, the fineness of cement is vital for various properties of concrete including workability, gypsum requirement, and long-term behavior. The fineness of cement is represented in terms of the specific surface of cement which is typically measured in square meters per kilogram, with several methods available for this determination.
Direct...
Direct...