Solar regeneration of powdered activated carbon impregnated with visible-light responsive photocatalyst: factors...

This study demonstrated a green technique to regenerate spent powdered activated carbon (AC) using solar photocatalysis. The AC was impregnated with a photocatalyst photoexcitable under visible-light irradiation to yield a solar regenerable composite, namely nitrogen-doped titanium dioxide (N-TiO(2)/AC). This composite exhibited bifunctional adsorptive-photocatalytic characteristics. Contaminants of emerging environmental concern, i.e. bisphenol-A (BPA), sulfamethazine (SMZ) and clofibric acid (CFA) which exhibited varying affinities for AC were chosen as target pollutants. The adsorption of BPA and SMZ by the N-TiO(2)/AC was significantly higher than that of CFA. The performance of solar photocatalytic regeneration (SPR) of the spent N-TiO(2)/AC composite generally increased with light intensity, N-TiO(2) loading and temperature. The regeneration efficiency (RE) for CFA-loaded spent composite was the highest compared to the other pollutant-loaded spent composites, achieving 77% within 8h of solar irradiation (765 W m(-2)). The rate-limiting process was pollutant desorption from the interior AC sorption sites. A kinetic model was developed to predict the transient concentration of the sorbate remaining in the spent composite during SPR. Comparison studies using solvent extraction technique indicated a different order of RE for the three pollutants, attributable to their varying solubilities in the aqueous and organic solvents.