Strain dependence of polarization and piezoelectric response in epitaxial BiFeO3 thin films

Epitaxial strain has recently emerged as a powerful means to engineer the properties of ferroelectric thin films, for instance to enhance the ferroelectric Curie temperature (T(C)) in BaTiO(3). However, in multiferroic BiFeO(3) thin films an unanticipated strain-driven decrease of T(C) was reported and ascribed to the peculiar competition between polar and antiferrodistortive instabilities. Here, we report a systematic characterization of the room-temperature ferroelectric and piezoelectric properties for strain levels ranging between -2.5% and +1%. We find that polarization and the piezoelectric coefficient increase by about 20% and 250%, respectively, in this strain range. These trends are well reproduced by first-principles-based techniques.