Influence of surface-attachment functionality on the aggregation, persistence, and electron-transfer reactivity of...

Chalcogenorhodamine dyes bearing phosphonic acids and carboxylic acids were compared as sensitizers of nanocrystalline TiO(2) in dye-sensitized solar cells (DSSCs). The dyes were constructed around a 3,6-bis(dimethylamino)chalcogenoxanthylium core and varied in the 9 substituent: 5-carboxythien-2-yl in dyes 1-E (E = O, Se), 4-carboxyphenyl in dyes 2-E (E = O, S), 5-phosphonothien-2-yl in dyes 3-E (E = O, Se), and 4-phosphonophenyl in dyes 4-E (E = O, Se). All dyes adsorbed to TiO(2) as mixtures of H aggregates and monomers, which exhibited broadened absorption spectra relative to those of purely amorphous monolayers. Surface coverages of dyes and the extent of H aggregation varied minimally with the surface-attachment functionality, the structure of the 9-aryl group, and the identity of the chalcogen heteroatom. Carboxylic acid-functionalized dyes 1-E and 2-E desorbed rapidly and completely from TiO(2) into acidified CH(3)CN, but phosphonic acid-functionalized dyes 3-E and 4-E persisted on TiO(2) for days. Short-circuit photocurrent action spectra of DSSCs corresponded closely to the absorptance spectra of dye-functionalized films; thus, H aggregation did not decrease the electron-injection yield or charge-collection efficiency. Maximum monochromatic incident photon-to-current efficiencies (IPCEs) of DSSCs ranged from 53 to 95% and were slightly higher for carboxylic acid-functionalized dyes 1-E and 2-E. Power-conversion efficiencies of DSSCs under white-light illumination were low (<1%), suggesting that dye regeneration was inefficient at high light intensities. The photoelectrochemical performance (under monochromatic or white-light illumination) of 1-E and 2-E decayed significantly within 20-80 min of the assembly of DSSCs, primarily because of the desorption of the dyes. In contrast, the performance of phosphonic acid-functionalized dyes remained stable or improved slightly on similar timescales. Thus, replacing carboxylic acids with phosphonic acids increased the inertness of chalcogenorhodamine-TiO(2) interfaces without greatly impacting the aggregation of dyes or the interfacial electron-transfer reactivity.