Plasmonic light trapping in thin-film silicon solar cells with improved self-assembled silver nanoparticles

Plasmonic metal nanoparticles are of great interest for light trapping in thin-film silicon solar cells. In this Letter, we demonstrate experimentally that a back reflector with plasmonic Ag nanoparticles can provide light-trapping performance comparable to state-of-the-art random textures in n-i-p amorphous silicon solar cells. This conclusion is based on the comparison to high performance n-i-p solar cell and state-of-the-art efficiency p-i-n solar cells deposited on the Asahi VU-type glass. With the plasmonic back reflector a gain of 2 mA/cm(2) in short-circuit current density was obtained without any deterioration of open circuit voltage or fill factor compared to the solar cell on a flat back reflector. The excellent light trapping is a result of strong light scattering and low parasitic absorption of self-assembled Ag nanoparticles embedded in the back reflector. The plasmonic back reflector provides a high degree of light trapping with a haze in reflection greater than 80% throughout the wavelength range 520-1100 nm. The high performance of plasmonic back reflector is attributed to improvements in the self-assembly technique, which result in a lower surface coverage and fewer small and irregular nanoparticles.