In vitro shear bond strength of resin-based luting cements to dentin

The aim of this study was to determine how resin cement, self-adhesive resin cement, and resin-modified glass ionomer cement affected shear bond strength to dentin. Sixty composite resin disks (3 mm in diameter x 3 mm in length) were prepared and divided into four groups (n = 15): Group 1, composite disk bonded to dentin with composite resin and a bonding agent; Group 2, composite disk bonded to dentin with a self-adhesive resin cement; Group 3, composite disk bonded to dentin with a different self-adhesive resin cement; and Group 4, composite disk bonded to dentin with a resin-modified glass ionomer cement. The composite resin was loaded into a syringe (internal diameter 3 mm), photocured in an oven, and cut into 3 mm slices with a low-speed saw. The samples were bonded to dentin per the manufacturer's instructions. All specimens were stored in distilled water (at 37 degrees C) for 24 hours. The shear bond strength test was conducted using a universal testing machine at a crosshead speed of 0.5 mm/min until failure. Conventional resin cement and a bonding agent exhibited significantly higher shear bond strength values than all other materials tested.