A fabrication strategy for nanosized zero valent iron (nZVI)-polymeric anion exchanger composites with tunable...

To reveal how the distribution of nanoscale zero-valent iron (nZVI) affect their reduction efficiency of its polymer-based composites and to further develop a simple strategy to tune the structure of the composites, we prepared four nZVI-polymerstyrene anion exchanger composites with similar nZVI loadings (13.5-14.4 Fe % in mass) but different distributions just through varying the concentration of NaBH(4) (0.9, 1.8, 3.6, and 7.2% in mass) solution during reduction of nZVI precursor (FeCl(4)(-) anions). As observed by SEM-EDX images, increasing the NaBH(4) concentration resulted in a more uniform nZVI distribution within the polymer, and thereto higher NH(4)(+)N production, faster reaction rate and more gaseous products during its reduction of nitrate and nitrite. nZVI distribution of the composites was suggested to greatly depend upon two processes, the hydrolyzation of anionic FeCl(4)(-) into cationic Fe(3+) and the reduction of both Fe(III) species by NaBH(4). Higher NaBH(4) concentration favored its faster diffusion into the inside polymer and in situ reduction of Fe(III) species into nZVI, causing a more uniform nZVI distribution. The results reported herein suggest that adjusting the NaBH(4) concentration was a simple and effective method to control the nZVI distribution in the supporting polymers, and indirectly tune the reactivity of the resultant nZVI hybrids.