A facile solution-phase approach to transparent and conducting ITO nanocrystal assemblies

Monodisperse 11 nm indium tin oxide (ITO) nanocrystals (NCs) were synthesized by thermal decomposition of indium acetylacetonate, In(acac)(3), and tin bis(acetylacetonate)dichloride, Sn(acac)(2)Cl(2), at 270 °C in 1-octadecene with oleylamine and oleic acid as surfactants. Dispersed in hexane, these ITO NCs were spin-cast on centimeter-wide glass substrates, forming uniform ITO NC assemblies with root-mean-square roughness of 2.9 nm. The assembly thickness was controlled by ITO NC concentrations in hexane and rotation speeds of the spin coater. Via controlled thermal annealing at 300 °C for 6 h under Ar and 5% H(2), the ITO NC assemblies became conductive and transparent with the 146 nm-thick assembly showing 5.2 × 10(-3) Ω·cm (R(s) = 356 Ω/sq) resistivity and 93% transparency in the visible spectral range--the best values ever reported for ITO NC assemblies prepared from solution phase processes. The stable hexane dispersion of ITO NCs was also readily spin-cast on polyimide (T(g) ~360 °C), and the resultant ITO assembly exhibited a comparable conductivity and transparency to the assembly on a glass substrate. The reported synthesis and assembly provide a promising solution to the fabrication of transparent and conducting ITO NCs on flexible substrates for optoelectronic applications.