In-situ fabrication of AAO template without oxide barrier layer and its applications
Jiewu Cui1, Yucheng Wu, Yan Wang
1School of Materials Science and Engineering, Hefei University of Technology, Hefei 230009, PR China.
Abstract:
Porous anodic aluminum oxide (AAO) film is the most widely used template in combination with electrodeposition (ED) method to fabricate one-dimensional nanostructures such as nanowires, nanotubes and nanorods. However, the existing oxide barrier layer after the anodization blocks the application of AAO template in synthesis of nanostructures via direct electrodeposition. In this paper, AAO template without oxide barrier layer was successfully fabricated by stepwise voltage decrement; influence of two types of stepwise voltage decrement on the removal of oxide barrier layer was introduced. Field Emission Scanning Electron Microscopy (FESEM) images indicated that stepwise voltage decrement could make the oxide layer thin effectively. Meanwhile, highly ordered gold nanowire arrays were fabricated by using direct electrodeposition method based on AAO template with the second anodization process with stepwise voltage decrement of 1 V/min, FESEM image showed that as-prepared gold nanowires are uniform in diameter and the diameter is in accordance with the diameter of AAO template pores. XRD pattern revealed that gold nanowires were indexed as face-centered cubic phase.
More Related Videos
10:27Simultaneous Multi-surface Anodizations and Stair-like Reverse Biases Detachment of Anodic Aluminum Oxides in Sulfuric and Oxalic Acid Electrolyte
Published on: October 5, 2017
11:24Fabrication of Gradient Nanopattern by Thermal Nanoimprinting Technique and Screening of the Response of Human Endothelial Colony-forming Cells
Published on: July 1, 2018