Construction and evaluation of high-quality n-ZnO nanorod/p-diamond heterojunctions

Vertically-aligned ZnO nanorods (NRs) arrays were synthesized by a low-temperature solution method on boron-doped diamond (BDD) films. The morphology, growth direction, and crystallinity of the ZnO NRs were studied by scanning electron microscopy, X-ray diffraction and cathodoluminescence. Electrical characterization of the ZnO NR/BBD heterostructures revealed characteristic p-n junction properties with an on/off ratio of about 50 at +/- 4 V and a small reverse leakage current approximately 1 microA. Moreover, the junctions showed an ideality factor around 1.0 at a low forward voltage from 0 to 0.3 V and about 2.1 for an increased voltage ranging from 1.2 to 3.0 V, being consistent with that of an ideal diode according to the Sah-Noyce-Shockley theory.