Microstructure evolution and development of annealed Ni/Au contacts to GaN nanowires

The development of Ni/Au contacts to Mg-doped GaN nanowires (NWs) is examined. Unlike Ni/Au contacts to planar GaN, current-voltage (I-V) measurements of Mg-doped nanowire devices frequently exhibit a strong degradation after annealing in N(2)/O(2). This degradation originates from the poor wetting behavior of Ni and Au on SiO(2) and the excessive void formation that occurs at the metal/NW and metal/oxide interfaces. The void formation can cause cracking and delamination of the metal film as well as reduce the contact area at the metal/NW interface, which increases the resistance. The morphology and composition of the annealed Ni/Au contacts on SiO(2) and the p-GaN films were investigated by scanning electron microscopy (SEM), energy-dispersive x-ray spectroscopy (EDS) and x-ray diffraction (XRD) measurements. Adhesion experiments were performed in order to determine the degree of adhesion of the Ni/Au films to the SiO(2) as well as observe and analyze the morphology of the film's underside by SEM. Device degradation from annealing was prevented through the use of a specific adhesion layer of Ti/Al/Ni deposited prior to the nanowire dispersal and Ni/Au deposition. I-V measurements of NW devices fabricated using this adhesion layer showed a decrease in resistance after annealing, whereas all others showed an increase in resistance. Transmission electron microscopy (TEM) on a cross-section of a NW with Ni/Au contacts and a Ti/Al/Ni adhesion layer showed a lack of void formation at the contact/NW interface. Results of the XRD and TEM analysis of the NW contact structure using a Ti/Al/Ni adhesion layer suggests Al alloying of the Ni/Au contact increases the adhesion and stability of the metal film as well as prevents excessive void formation at the contact/NW interface.