The plasticizing mechanism and effect of calcium chloride on starch/poly(vinyl alcohol) films

Xiancai Jiang1, Ting Jiang, Lingling Gan

  • 1State Key Laboratory of Polymer Materials Engineering, Chengdu 610065, China.

Carbohydrate Polymers
|September 5, 2012
PubMed

More Related Videos

Calcium Carbonate Formation in the Presence of Biopolymeric Additives09:31

Calcium Carbonate Formation in the Presence of Biopolymeric Additives

Published on: May 14, 2019

Development and Characterization of Fusidic Acid-Loaded Alginate-Aloe vera Based Hydrogel Film04:09

Development and Characterization of Fusidic Acid-Loaded Alginate-Aloe vera Based Hydrogel Film

Published on: December 13, 2024

Related Concept Videos

Plasticizers01:31

Plasticizers

Water-reducers, or plasticizers, are chemical admixtures used in concrete to improve strength and workability. These additives reduce the water-cement ratio without compromising workability, lower the cement content while maintaining the same workability, or increase workability to assist concrete placement in inaccessible areas.
Plasticizers function by using surface-active agents to create repulsive electrostatic forces between cement particles. This dispersion enhances the concrete's...
Polymer Classification: Stereospecificity01:26

Polymer Classification: Stereospecificity

Polymerization generates chiral centers along the entire backbone of a polymer chain. Accordingly, the stereochemistry of the substituent group has a significant effect on polymer properties. Polymers formed from monosubstituted alkene monomers feature chiral carbons at every alternate position in the polymer backbone. Relative to the predominant orientation of substituents at the adjacent chiral carbons, the polymer can exist in three different configurations: isotactic, syndiotactic, and...
Polymer Classification: Crystallinity01:21

Polymer Classification: Crystallinity

Unlike ionic or small covalent molecules, polymers do not form crystalline solids due to the diffusion limitations of their long-chain structures. However, polymers contain microscopic crystalline domains separated by amorphous domains.
Crystalline domains are the regions where polymer chains are aligned in an orderly manner and held together in proximity by intermolecular forces. For example, chains in the crystalline domains of polyethylene and nylon are bound together by van der Waals...
Factors Affecting Solubility04:01

Factors Affecting Solubility

Compared with pure water, the solubility of an ionic compound is less in aqueous solutions containing a common ion (one also produced by dissolution of the ionic compound). This is an example of a phenomenon known as the common ion effect, which is a consequence of the law of mass action that may be explained using Le Chȃtelier’s principle. Consider the dissolution of silver iodide:
Cationic Chain-Growth Polymerization: Mechanism00:57

Cationic Chain-Growth Polymerization: Mechanism

The cationic polymerization mechanism consists of three steps: initiation, propagation, and termination. In the initiation step of the polymerization process, the π bond of a monomer gets protonated by the Lewis acid catalyst, which is formed from boron trifluoride and water. The protonation of the π bond generates a carbocation stabilized by the electron‐donating group. In the propagation step, the π bond of the second monomer acts as a nucleophile and attacks the generated carbocation,...
Ionic Strength: Effects on Chemical Equilibria01:19

Ionic Strength: Effects on Chemical Equilibria

The addition of an inert ionic compound increases the solubility of a sparingly soluble salt. For example, adding potassium nitrate to a saturated solution of calcium sulfate significantly enhances the solubility of calcium sulfate. Le Châtelier's principle cannot predict this shift in the equilibrium. Instead, this could be explained in terms of changes in the effective concentration of the ions in solution in the presence of added inert salt.
In this solution, the primary cation—the calcium...