Electrospun fibre diameter, not alignment, affects mesenchymal stem cell differentiation into the tendon/ligament...

Efforts to develop engineered tendons and ligaments have focused on the use of a biomaterial scaffold and a stem cell source. However, the ideal scaffold microenvironment to promote stem cell differentiation and development of organized extracellular matrix is unknown. Through electrospinning, fibre scaffolds can be designed with tailorable architectures to mimic the intended tissue. In this study, the effects of fibre diameter and orientation were examined by electrospinning thin mats, consisting of small (< 1 µm), medium (1-2 µm) or large (> 2 µm) diameter fibres with either random or aligned fibre orientation. C3H10T1/2 model stem cells were cultured on the six different electrospun mats, as well as smooth spin-coated films, and the morphology, growth and expression of tendon/ligament genes were evaluated. The results demonstrated that fibre diameter affects cellular behaviour more significantly than fibre alignment. Initially, cell density was greater on the small fibre diameter mats, but similar cell densities were found on all mats after an additional week in culture. After 2 weeks, gene expression of collagen 1α1 and decorin was increased on all mats compared to films. Expression of the tendon/ligament transcription factor scleraxis was suppressed on all electrospun mats relative to spin-coated films, but expression on the large-diameter fibre mats was consistently greater than on the medium-diameter fibre mats. These results suggest that larger-diameter fibres (e.g. > 2 µm) may be more suitable for in vitro development of a tendon/ligament tissue.