Thermodynamic determination of the metal/semiconductor separation of carbon nanotubes using hydrogels

The metal/semiconductor separation of single-wall carbon nanotubes (SWCNTs) using hydrogels, such as agarose gel and Sephacryl, together with sodium dodecyl sulfate is one of the most successful techniques necessary for industrial applications. Despite recent improvements in the technique, little is known about the separation mechanism. Here, we show that SWCNTs are reversibly adsorbed onto hydrogels in the presence of sodium dodecyl sulfate. The results enabled us to examine the thermodynamics of the adsorption reaction and thereby elucidate the separation mechanism. The adsorbability of SWCNTs onto the hydrogels was described by the standard Gibbs free energy for the adsorption, as well as the area of the hydrogels allowing the adsorption. We demonstrated, for the first time, that the free energy of adsorption for semiconducting SWCNTs was 0-12 kJ/mol lower than that for metallic SWCNTs in the temperature range of 290-320 K (e.g., ca. -4 kJ/mol for the agarose gel and ca. -9 kJ/mol for Sephacryl at 300 K), which permits metal/semiconductor separation. Importantly, the difference in the free energy was attributed to the difference in the enthalpy of adsorption: the enthalpy of adsorption of metallic SWCNTs was ca. 70 kJ/mol higher than that of semiconducting SWCNTs. Thus, the enthalpy of adsorption was found to be an important parameter in the metal/semiconductor separation of SWCNTs using hydrogels. In addition, the thermodynamic parameters depended on the hydrogel type and the surfactant concentration, which is most likely why under certain conditions hydrogels and surfactants produce different separations, e.g., chirality-selective or diameter-selective separation.