Laser heating of gold nanospheres functionalized with octreotide: in vitro effect on HeLa cell viability

The aim of this study was to assess the effect of laser heating a well-characterized gold nanoparticle (AuNP)-octreotide system on HeLa cell viability, to evaluate its potential as a suitable agent for plasmonic photothermal therapy.

Octreotide is a synthetic peptide derivative of somatostatin with an effect on the survival of HeLa cells. Peptides bound to AuNPs are biocompatible and stable multimeric systems with target-specific molecular recognition.

Octreotide was conjugated to AuNPs (∼20 nm) by spontaneous reaction with the thiol groups. The nanoconjugate was characterized by transmission electron microscopy (TEM), Fourier transform infrared spectroscopy (FT-IR), ultraviolet visible spectroscopy (UV-Vis), X-ray photoelectron spectroscopy (XPS), and Raman spectroscopy. Irradiation experiments were conducted using an Nd:YAG laser pulsed for 5 ns at 532 nm with a repetition rate of 10 Hz for up to 6 min while delivering an average irradiance of 0.65 W/cm(2). HeLa cells were incubated at 37°C (1) with AuNP-citrate, (2) with AuNP-octreotide, or (3) without nanoparticles.

After laser irradiation, the presence of AuNP caused a significant increase in the temperature of the medium (48°C vs. 38.3°C of that without AuNP). The AuNP-octreotide system resulted in a significant decrease in cell viability of up to 6 % compared with the AuNP-citrate system (15.8±2.1%). Two possible mechanisms could be at play: (1) octreotide alone exerts an effect on survival HeLa cells, or (2) the release of heat (∼727°C per nanoparticle) in the membranes or cytoplasm of the cells caused by the interaction between AuNP-octreotide and somatostatin receptors reduced viability.

The AuNP-octreotide system exhibited properties suitable for plasmonic photothermal therapy in the treatment of cervical cancer.