Peak stress intensity factor governs crack propagation velocity in crosslinked ultrahigh-molecular-weight

Abhiram Sirimamilla1, Jevan Furmanski, Clare Rimnac

  • 1Musculoskeletal Mechanics and Materials Lab, Mechanical and Aerospace Engineering Department, Case Western Reserve University, Cleveland, Ohio, USA.

Journal of Biomedical Materials Research. Part B, Applied Biomaterials
|November 21, 2012
PubMed

More Related Videos

Predicting Catalyst Extrudate Breakage Based on the Modulus of Rupture09:53

Predicting Catalyst Extrudate Breakage Based on the Modulus of Rupture

Published on: May 13, 2018

Studying Large Amplitude Oscillatory Shear Response of Soft Materials06:07

Studying Large Amplitude Oscillatory Shear Response of Soft Materials

Published on: April 25, 2019

Related Concept Videos

Stress Concentrations01:24

Stress Concentrations

Stress concentration is when stress intensifies near discontinuities such as holes or abrupt cross-sectional changes in a structural member. This localized stress can often surpass the average stress within the member. The stress distribution in flat bars, either with a circular hole or varying widths connected by fillets, can be determined experimentally using a photoelastic method. The results are based on ratios of geometric parameters like the ratio of the hole's radius to the smaller width...
Stress Concentrations01:13

Stress Concentrations

The concept of stress concentration is crucial for understanding how materials respond under bending stresses, particularly when there are irregularities or discontinuities in the material's geometry. Normally, stress in a symmetric member subjected to pure bending is assumed to be uniformly distributed across the entire cross-section. However, this assumption does not hold when there are variations in the cross-sectional geometry or the presence of notches and holes.
The stress concentration...
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
Members Made of Elastoplastic Material01:19

Members Made of Elastoplastic Material

The behavior of elastoplastic materials under bending stresses, particularly in structural members with rectangular cross-sections, is crucial for predicting material responses and understanding failure modes. Initially, when a bending moment is applied, the stress distribution across the section follows Hooke's Law and is linear and elastic. This distribution means the stress increases from the neutral axis to the maximum at the outer fibers, up to the elastic limit.
As the bending moment...
Plastic Behavior01:21

Plastic Behavior

A material's elastic behavior is characterized by the disappearance of stress once the load is removed, allowing the material to return to its original state. However, when stress surpasses the yield point, yielding commences, marking the onset of plastic deformation or permanent set. This change from elastic to plastic behavior is influenced by the peak stress value and the duration before the load is removed. An intriguing observation occurs when a specimen is loaded, unloaded, and reloaded.
Relation between Poisson's ratio, Modulus of Elasticity and Modulus of Rigidity01:15

Relation between Poisson's ratio, Modulus of Elasticity and Modulus of Rigidity

Deformation occurs in axial and transverse directions when an axial load is applied to a slender bar. This deformation impacts the cubic element within the bar, transforming it into either a rectangular parallelepiped or a rhombus, contingent on its orientation. This transformation process induces shearing strain. Axial loading elicits both shearing and normal strains. Applying an axial load instigates equal normal and shearing stresses on elements oriented at a 45° angle to the load axis.