Some studies on evaluation of degradation in composite adhesive joints using ultrasonic techniques

Experimental and theoretical studies on degradation of composite-epoxy adhesive joints were carried out on samples having different interfacial and cohesive properties. Oblique incidence ultrasonic inspection of bonded joints revealed that degradation in the adhesive can be measured by significant variation in reflection amplitude as also by a shift in the minima of reflection spectrum. It was observed that severe degradation of the adhesive leads to failure dominated by interfacial mode. Through this investigation it is demonstrated that a correlation exists between the bond strength and a frequency shift in reflection minimum. The experimental data was validated using analytical models. Though both bulk adhesive degradation and interfacial degradation influences the shift in spectrum minimum, the contribution of the latter was found to be significant. An inversion algorithm was used to determine the interfacial transverse stiffness using the experimental oblique reflection spectrum. The spectrum shift was found to depend on the value of interfacial transverse stiffness using which a qualitative assessment can be made on the integrity of the joint.