Structural, microstructural and magnetic properties of (La(1-x)Ca(x))MnO3 nanoparticles
A Martinelli1, M Ferretti, C Castellano
1CNR-SPIN, Corso Perrone 24, I-16152 Genova, Italy. alberto.martinelli@spin.cnr.it
Abstract:
The crystal and magnetic structures of 10 and 20 nm sized (La1-xCax)MnO3 (x = 0.37, 0.50, 0.75) have been investigated between 5 and 300 K by means of Rietveld refinement of neutron powder diffraction data, coupled with transmission electron microscope observation and magnetization measurements. TEM observation reveals that nanoparticles are strongly affected by strain fields, probably originating from surface pressure. Irrespective of the composition, charge and orbital orderings are suppressed and Fz and Cy spin orderings coexist at low temperature; Cy and Fz orderings likely occur within the strained regions of the nanoparticles and in the matrix respectively. Moreover Gz and Az orderings are sometimes observed, and are likely to be taking place at the border of the strained regions.
Related Concept Videos
03:02Colors and Magnetism
When atoms or molecules absorb light at the proper frequency, their electrons are excited to higher-energy orbitals. For many main group atoms and molecules, the absorbed photons are in the ultraviolet range of the electromagnetic spectrum, which cannot be detected by the human eye. For coordination compounds, the energy difference between the d orbitals often allows photons in the visible range to be absorbed and emitted, which is seen as colors by the human eye.
01:29Imperfections in Crystal Structure: Non-Stoichiometric Defects