Influence of polymerization time and depth of cure of resin composites determined by Vickers hardness

Adequate polymerization of resin composites could be considered as a crucial factor in obtaining good clinical performance, particularly in stress-bearing areas. An insufficient curing degree affects the resin composite's chemical properties The current in vitro study evaluated the influence of polymerization time and depth of cure of six commercial resin composites by Vickers microhardness (VK).

SIX RESIN COMPOSITES WERE SELECTED: Three microhybrid (Esthet.X HD, Amaris, Filtek Silorane), two nanohybrid (Grandio, Ceram.X mono), and one nanofilled (Filtek Supreme XT). The VK of the surface was determined by a microhardness tester using a Vickers diamond indenter and a 200 g load applied for 15 s. The bottom to top mean VK ratio was calculated using the formula: Hardness ratio = VK of bottom surface/VK of top surface. Vickers hardness values of test materials during exposure time of 20 and 40 s and depths of cure of 2 and 3 mm were determined and compared. Data were analyzed using analysis of variance (ANOVA) test.

For all the tested materials and with all the exposure time periods, hardness ratio was higher than the minimum value indicated in literature (0.8). Exposure time and depth of cure did not affect hardness ratio values for Filtek Silorane, Grandio, and Filtek Supreme XT.

Among the materials tested, the nanofilled and the nanohybrid resin composites were rather insensible to thickness variations. Miicrohybrid composites, instead, had features different from one another.