Influence of water vapour and carbon dioxide on free lime during storage at 80 °C, studied by Raman spectroscopy

Micro-Raman spectroscopy has been used to follow the reaction of free lime (CaO) exposed for 24h to moist air at 80 °C under conditions of different relative humidities (10-80% RH). X-ray diffraction and SEM imaging were applied as complementary techniques. The conversion of lime to calcium hydroxide and its subsequent carbonation to various calcium carbonate polymorphs was found to strongly depend on the relative humidity. At low RH (10-20%), only Raman spectroscopy revealed the formation of early amorphous CaCO3 which in the XRD patterns was detected only at ≥40% RH. However, XRD analysis could identify the crystalline polymorphs formed at higher relative humidities. Thus, between 20 and 60% RH, all three CaCO3 polymorphs (calcite, aragonite and vaterite) were observed via XRD whereas at high relative humidity (80%), calcite was the predominant reaction product. The results demonstrate the usefulness of Raman spectroscopy in the study of minor cement constituents and their reaction products on air, especially of amorphous character.