Oriented film growth of Ba(1-x)Sr(x)TiO3 dielectrics on glass substrates using 2D nanosheet seed layer

An approach to fabricate Ba0.5Sr0.5TiO3 (BST) films with a preferred orientation on a glass substrate by pulsed laser deposition was developed. To ensure a preferred crystallographic orientation, we utilized a molecularly thin Ca2Nb3O10 perovskite nanosheet as a seed layer and successfully fabricated BST films with a nearly perfect (100)-axis orientation. The 100 nm films after annealing at 450 °C in air showed a good dielectric performance (ε(r) > 400), which was comparable to the ε(r) value of epitaxially grown films with the same thickness. These results indicate that the nanosheet seed layer plays a crucial role in controlled film growth, realizing a nearly intrinsic performance of BST.