Bioactive plasma electrolytic oxidation coatings--the role of the composition, microstructure, and electrochemical

M Mohedano1, R Guzman, R Arrabal

  • 1Departamento de Ciencia de Materiales, Facultad de Ciencias Químicas, Universidad Complutense, 28040, Madrid, Spain.

Journal of Biomedical Materials Research. Part B, Applied Biomaterials
|June 8, 2013
PubMed

Keywords:
cell proliferationcoating(s)corrosionplasma electrolytic oxidationtitanium (alloys)

More Related Videos

Probing Surface Electrochemical Activity of Nanomaterials using a Hybrid Atomic Force Microscope-Scanning Electrochemical Microscope (AFM-SECM)08:31

Probing Surface Electrochemical Activity of Nanomaterials using a Hybrid Atomic Force Microscope-Scanning Electrochemical Microscope (AFM-SECM)

Published on: February 10, 2021

Localized Bathless Metal-Composite Plating via Electrostamping08:05

Localized Bathless Metal-Composite Plating via Electrostamping

Published on: September 22, 2020

Related Concept Videos

Corrosion02:49

Corrosion

The degradation of metals due to natural electrochemical processes is known as corrosion. Rust formation on iron, tarnishing of silver, and the blue-green patina that develops on copper are examples of corrosion. Corrosion involves the oxidation of metals. Sometimes it is protective, such as the oxidation of copper or aluminum, wherein a protective layer of metal oxide or its derivatives forms on the surface, protecting the underlying metal from further oxidation. In other cases, corrosion is...
Electrodeposition01:08

Electrodeposition

Electrodeposition is a technique used to separate an analyte from interferents by electrochemical processes. Here, the analyte is a metal ion that can be deposited on an electrode immersed in the sample solution. The electrochemical setup consists of an anode and a cathode. When an electric current is applied to the setup, oxidation occurs at the anode. At the cathode, which consists of a large metal surface, metal ions undergo reduction and deposit onto the surface.
Electrodeposition can...
Corrosion of Reinforcement01:27

Corrosion of Reinforcement

The corrosion of steel reinforcement within concrete is a process influenced by the material's inherent properties and external factors. The high pH level of around 13, provided by calcium hydroxide present in concrete, initially protects the steel reinforcement by promoting the formation of a passive iron oxide layer on its surface.
However, over time and under certain conditions like carbonation, chloride ingress, and cracking this protective state can be compromised. Steel has areas with...
Microbial Corrosion01:24

Microbial Corrosion

Microbiologically Influenced Corrosion (MIC) is a significant form of material degradation caused by the metabolic activities of microorganisms. This phenomenon poses substantial challenges across various industries, including oil and gas, maritime, and water treatment sectors.MIC occurs when microorganisms, such as bacteria, archaea, and fungi, colonize metal surfaces, forming biofilms that alter the local electrochemical environment. These biofilms can lead to the production of corrosive...
Electrogravimetric Analysis: Overview01:30

Electrogravimetric Analysis: Overview

Electrogravimetric analysis measures the weight of an analyte deposited electrolytically onto a suitable working electrode. This method involves applying a potential to a pre-weighed electrode submerged in a solution, which results in the desired substance being deposited through reduction at the cathode or oxidation at the anode. The electrode's weight is recorded after deposition, and the difference in weight gives the analyte's weight in the solution.
To test the completeness of the...
Radical Autoxidation01:20

Radical Autoxidation

The oxidation of an organic compound in the presence of air or oxygen is called autoxidation. For example, cumene reacts with oxygen to form hydroperoxide. Autoxidation involves initiation, propagation, and termination steps. Many organic compounds are susceptible to autoxidation—especially ethers in the presence of oxygen, which form hydroperoxides. Even though this reaction is slow, old ether bottles contain small amounts of peroxide, which leads to laboratory explosions during ether...