Scanning Electron Microscopic Evaluation of Surface Defects of Remover Retreatment File After Single and Multiple Uses
Published on: October 11, 2024
Effects of multiple root canal usage on the surface topography and fracture of two different Ni-Ti rotary file
Jojo Kottoor1, Natanasabapathy Velmurugan, Velayutham Gopikrishna
1Department of Conservative Dentistry and Endodontics, Mar Baselios Dental College, Kothamangalam, Ernakulam, Kerala, India.
Aim:
The purpose of this study was to evaluate the effect of multiple root canal usage on the surface topography and fracture of Twisted File (TF) and ProTaper (PT) rotary Ni-Ti file systems, using scanning electron microscope (SEM).
Materials And Methods:
Ten sets of PT and TF instruments were used to prepare the mesial canals of mandibular first molars. TF 25, 0.06 taper and PT F1 instruments were analyzed by SEM when new and thereafter every three root canal usages. This sequence was repeated for both the TF and PT groups until 12 uses. Two images of the instrument were recorded, one of the instrument tip and the other 5 mm from the tip, both at × 100 magnification. The sequential use was continued till the instrument fractured and the number of root canal usages for the file to fracture was noted. All fracture surfaces were examined under the SEM.
Results:
Fresh TF instruments showed no surface wear when compared to PT instruments (P < 0.05). Spiral distortion scores remained the same for both the groups till the 6 th usage (P > 0.05), while at the 9 th usage TF showed a steep increase in the spiral distortion score when compared to PT (P < 0.05). PT instruments fractured at a mean root canal usage of 17.4, while TF instruments showed a mean root canal usage of 11.8. Fractographically, all the TF instruments failed due to torsion, while all the PT instruments failed because of cyclic fatigue.
Conclusion:
PT instruments showed more resistance to fracture than TF instruments.