Enhancement of phase separation and superconductivity in Mn-doped K0.8Fe2-yMnySe2 crystals

Single crystals of K0.8Fe2-yMnySe2 with slight Mn doping have been grown by a self-flux method. X-ray diffraction measurements show enhanced phase separation with increasing Mn doping in the compounds. The superconducting transition temperature increases to Tc,onset ∼ 46.1 K for the sample with y ∼ 0.03, as observed by electrical transport measurements. Our results demonstrate that the doping of Mn does not suppress the superconductivity, and on the contrary increases the superconducting shield fraction and transition temperature, an effect which may originate from the Mn dopant's high preference to fill into iron vacancies in the Mn-doped samples. It suggests that the Mn dopant can induce a local lattice strain or distortion that profitably modifies the microstructure of the superconducting/metallic phase, leading to superconductivity of the compound.