Comparative evaluation of bond strengths of different core materials with various luting agents used for cast crown...

The coronal cast restoration continues to be used commonly to restore mutilated, endodontically treated teeth. The tensile bond strength of luting cements is of critical importance as many of failures are at the core and the crown interface. An invitro study with aim to evaluate and compare bond strengths of luting cements between different core materials and cast crowns. A total of 45 extracted identical mandibular second premolars were endodontically treated and divided into 3 groups of 15 each. Specimens in first group were restored with cast post and core (Group C), and specimens in second group were restored with stainless steel parapost and composite core material (Group B) and specimens in third group were restored with stainless steel parapost and glass ionomer core build (Group G). Standardized crown preparation was done for all the specimens to receive cast crowns. Each group was further divided into 3 subgroups and were cemented using 3 different luting cements namely, resin cement, polycarboxylate cement, glass ionomer cement (Type I). The samples of each subgroup (n = 5) were subjected to tensile testing using Universal Testing Machine at a crosshead speed of 2 mm/min till the dislodgement of crown from the core surface was observed. The bond strengths were significantly different according one way ANOVA (F-150.76 and p < 0.0000). The results of the study showed that the specimens cemented with resin cement in cast core, composite core and glass ionomer core exhibited significantly higher bond strengths as compared to specimens cemented with glass ionomer and polycarboxylate cement. Composite resin core and resin cement combinations were superior to all other cement and core combinations tested.