Optimization of the magnetoelectric response of poly(vinylidene fluoride)/epoxy/Vitrovac laminates

The effect of the bonding layer type and piezoelectric layer thickness on the magnetoelectric (ME) response of layered poly(vinylidene fluoride) (PVDF)/epoxy/Vitrovac composites is reported. Three distinct epoxy types were tested, commercially known as M-Bond, Devcon, and Stycast. The main differences among them are their different mechanical characteristics, in particular the value of the Young modulus, and the coupling with the polymer and Vitrovac (Fe39Ni39Mo4Si6B12) layers of the laminate. The laminated composites prepared with M-Bond epoxy exhibit the highest ME coupling. Experimental results also show that the ME response increases with increasing PVDF thickness, the highest ME response of 53 V·cm(-1)·Oe(-1) being obtained for a 110 μm thick PVDF/M-Bond epoxy/Vitrovac laminate. The behavior of the ME laminates with increasing temperatures up to 90 °C shows a decrease of more than 80% in the ME response of the laminate, explained by the deteriorated coupling between the different layers. A two-dimensional numerical model of the ME laminate composite based on the finite element method was used to evaluate the experimental results. A comparison between numerical and experimental data allows us to select the appropriate epoxy and to optimize the piezoelectric PVDF layer width to maximize the induced magnetoelectric voltage. The obtained results show the critical role of the bonding layer and piezoelectric layer thickness in the ME performance of laminate composites.