Nanoparticles in the zirconia-europium niobate system via hydrothermal route

The effect of the composition on the hydrothermal formation, structure, and properties of nanocrystalline luminescent materials in the zirconia (ZrO2)-europium niobate 1/4(Eu3NbO7) system was investigated. In the composition range 40 < or = ZrO2 mol% < or = 90, nanocrystalline particles with crystallite size 6.0-7.6 nm that were hydrothermally formed from the precursor solutions of NbCl5, ZrOCI2, and EuCl3 under weakly basic conditions at 240 degrees C showed cubic structure. The lattice parameter when estimated as a single cubic phase linearly decreased as the concentration of ZrO2 increased. The presence of zirconia component effectively promoted the formation of nanocrystals containing the niobate, Eu3NbO7 under hydrothermal condition. The nanocrystalline particles could be excited by ultraviolet light 395 nm (f-f transition) and emitted orange (590 nm) and red light (610 nm) corresponding to 5D0 --> 7F1 and 5D0 --> 7F2 transitions of Eu3+, respectively. The intensity of the electric dipole transition (5D0 --> 7F2) that was expressed in values relative to the magnetic dipole transition (5D0 --> 7F1) increased with increased heat-treatment temperature in the range from 950 to 1200 degrees C.