β-type Ti-10Mo-1.25Si-xZr biomaterials for applications in hard tissue replacements

In order to develop new β-type Ti-based biochemical materials, a series of Ti-10Mo-1.25Si-xZr (x=4-13) alloys were designed and prepared using vacuum arc melting method. Phase analysis and microstructural observation showed that all the as cast samples consisted of equiaxed β-Ti phase. With the increase of Zr content, the structure of grain boundary changed from semi-continuous network to denser granular, and the microstructure was refined. The solid solution effect of the β-phase stabilization elements (i.e. Mo, Zr and Si) predominantly determined the mechanical properties. These β-type Ti-10Mo-1.25Si-xZr biomaterials exhibited a good combination of high compressive strength, high yield stress, good plasticity, as well as rather low Young's modulus (in the range of 23.086 GPa-32.623 GPa), which may offer potential advantages in the applications in hard tissue replacements (HTRs).