Microhardness of dual-polymerizing resin cements and foundation composite resins for luting fiber-reinforced posts
Keiichi Yoshida1, Xiangfeng Meng2
1Assistant Professor, Clinic of Fixed Prosthodontics, Nagasaki University Hospital, Nagasaki, Japan.
Statement Of Problem:
The optimal luting material for fiber-reinforced posts to ensure the longevity of foundation restorations remains undetermined.
Purpose:
The purpose of this study was to evaluate the suitability of 3 dual-polymerizing resin cements and 2 dual-polymerizing foundation composite resins for luting fiber-reinforced posts by assessing their Knoop hardness number.
Material And Methods:
Five specimens of dual-polymerizing resin cements (SA Cement Automix, G-Cem LincAce, and Panavia F2.0) and 5 specimens of dual-polymerizing foundation composite resins (Clearfil DC Core Plus and Unifil Core EM) were polymerized from the top by irradiation for 40 seconds. Knoop hardness numbers were measured at depths of 0.5, 2.0, 4.0, 6.0, 8.0, and 10.0 mm at 0.5 hours and 7 days after irradiation. Data were statistically analyzed by repeated measures ANOVA, 1-way ANOVA, and the Tukey compromise post hoc test (α=.05).
Results:
At both times after irradiation, the 5 resins materials showed the highest Knoop hardness numbers at the 0.5-mm depth. At 7 days after irradiation, the Knoop hardness numbers of the resin materials did not differ significantly between the 8.0-mm and 10.0-mm depths (P>.05). For all materials, the Knoop hardness numbers at 7 days after irradiation were significantly higher than those at 0.5 hours after irradiation at all depths (P<.05). At 7 days after irradiation, the Knoop hardness numbers of the 5 resin materials were found to decrease in the following order: DC Core Plus, Unifil Core EM, Panavia F2.0, SA Cement Automix, and G-Cem LincAce (P<.05).
Conclusions:
The Knoop hardness number depends on the depth of the cavity, the length of time after irradiation, and the material brand. Although the Knoop hardness numbers of the 2 dual-polymerizing foundation composite resins were higher than those of the 3 dual-polymerizing resin cements, notable differences were seen among the 5 materials at all depths and at both times after irradiation.