Effects of molecular weight of grafted hyaluronic acid on wear initiation
Dong Woog Lee1, Xavier Banquy2, Saurabh Das1
1Chemical Engineering Department, University of California at Santa Barbara, Santa Barbara, CA, USA.
Abstract:
Hyaluronic acid (HA) of different molecular weights (Mw) was grafted onto mica surfaces to study the effects of Mw on the conformation and wear protection properties of a grafted HA (gHA) layer in lubricin (LUB) and bovine synovial fluid (BSF) using a surface forces apparatus. The Mw of gHA had significant effects on the wear pressure (Pw), at which point the wear initiates. Increasing the gHA Mw from 51 to 2590kDa increased Pw from 4 to 8MPa in LUB and from 15 to 31MPa in BSF. The 2590kDa gHA in BSF had the best wear protection (Pw∼31MPa), even though it exhibited the highest friction coefficient (μ∼0.35), indicating that a low μ does not necessarily result in good wear protection, as is often assumed. The normal force profile indicated that BSF confines the gHA structure, making it polymer brush-like, commonly considered as an excellent structure for boundary lubrication.
More Related Videos
06:05Author Spotlight: Enhancing Bone Regeneration with Vascularized Artificial Cartilage Integration
Published on: July 14, 2023
15:33Microwave-assisted Functionalization of Polyethylene glycol and On-resin Peptides for Use in Chain Polymerizations and Hydrogel Formation
Published on: October 29, 2013
Related Concept Videos
01:23Glycosaminoglycans
GAGS are found in the extracellular matrix of vertebrates, invertebrates, and bacteria. Due to their polar nature they attract water, and serve as excellent lubricants or shock absorbers in an animal body.
Hyaluronic...
01:08Molecular Weight of Step-Growth Polymers
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...