Photoinitiators in dentistry: a review

Polymerization of Resin Based Composites (RBCs) initiated by a light curing unit activating photoinitiators. Different RBCs require different light energy levels for proper curing. Manufacturers are now producing RBCs with more than one initiator and not all of these will be properly polymerised with blue LED lights. An added problem is that manufacturers do not always indicate the type of photoinitiators in their materials. This review discusses the importance of matching the spectral output of LCUs to the absorption spectra of RBCs and the consequences of spectral mismatch. Resin based composites (RBCs) were first introduced in the 1960s and with development of effective and reliable dentine bonding systems2, have been used routinely as a filling material for both anterior and posterior teeth. The early RBCs were either chemically cured two component materials or photo-initiated materials that used UV initiators in the beginning and then transitioned to visible light initiators such as camphorquinine which was introduced in 1978.3 The first report of a light curing material was of an ultraviolet (UV) cured fissure sealant. However, due to the limited penetration depth of the UV light and the potential health hazards, this system was quickly abandoned. The advancement of science yielded light curing materials which contributed to a significant clinical progress over the UV and chemically cured RBCs. Additional advancements to direct RBC restoration materials included luting agents for ceramic restorations, pit and fissure sealants and resin modified glass ionomers. Polymerization in an RBC is initiated by a light curing unit (LCU); this technology is based on the use of photoreactive systems that absorb light irradiation from the LCUs at appropriate wavelength. Then the photoinitiators contained in the RBCs, absorb the incoming photons from the LCU and the monomers in the molecular structure become excited and in that active state, there is a change from monomers into a polymer network. The success of this technology hinges on matching the spectral emission of the LCU with the requirements of the photoinitiator system to convert the monomers into a polymer network. The amount of activated photo initiator depends on the concentration of photoinitiator in the material, the number of photons to which the material is exposed and the energy of the photons (wavelength), the latter depending on the curing light.The most common photoinitiator in dental materials today is camphorquinone, which has a peak activity around 470 nanometres. The factors affecting polymerization include filler type, size and loading, the thickness and shade of the restorative material, the effectiveness of light transmission (eg. light guide tips being free from debris and scratches), exposure time, distance of the light source from the restorative material and light intensity. It is important to note that the photoinitiator activation occurs at specific wavelengths, in other words, the optimum efficiency is obtained when the peak absorptivity of the photoinitiator corresponds with the spectral emission from the LCU. Commercially available curing units have different light intensities and light sources, with energy levels in QTH, LED and other LCUs ranging from 300 to more than 2000 mW/cm.