Effect of the infrastructure material on the failure behavior of prosthetic crowns
Queli Nunes Sonza1, Alvaro Della Bona1, Márcia Borba1
1Post-graduate Program in Dentistry, Dental School, University of Passo Fundo, Passo Fundo, RS, Brazil.
Objectives:
To evaluate the effect of infrastructure (IS) material on the fracture behavior of prosthetic crowns.
Methods:
Restorations were fabricated using a metal die simulating a prepared tooth. Four groups were evaluated: YZ-C, Y-TZP (In-Ceram YZ, Vita) IS produced by CAD-CAM; IZ-C, In-Ceram Zirconia (Vita) IS produced by CAD-CAM; IZ-S, In-Ceram Zirconia (Vita) IS produced by slip-cast; MC, metal IS (control). The IS were veneered with porcelain and resin cemented to fiber-reinforced composite dies. Specimens were loaded in compression to failure using a universal testing machine. The 30° angle load was applied by a spherical piston, in 37°C distilled water. Fractography was performed using stereomicroscope and SEM. Data were statistically analyzed with Anova and Student-Newman-Keuls tests (α=0.05).
Results:
Significant differences were found between groups (p=0.022). MC showed the highest mean failure load, statistically similar to YZ-C. There was no statistical difference between YZ-C, IZ-C and IZ-S. MC and YZ-C showed no catastrophic failure. IZ-C and IZ-S showed chipping and catastrophic failures. The fracture behavior is similar to reported clinical failures.
Significance:
Considering the ceramic systems evaluated, YZ-C and MC crowns present greater fracture load and a more favorable failure mode than In-Ceram Zirconia crowns, regardless of the fabrication type (CAD-CAM or slip-cast).