Enhanced upconversion emission in colloidal (NaYF4:Er(3+))/NaYF4 core/shell nanoparticles excited at 1523 nm

In this work, we report on efficient visible and near-IR upconversion emissions in colloidal hexagonal-phase core/shell NaYF4:Er(3+)/NaYF4 nanoparticles (∼38  nm) under IR laser excitation at 1523 nm. Varying amounts of Er(3+) dopants were introduced into the core NaYF4:Er(3+) nanoparticles, revealing an optimized Er(3+) concentration of 10% for the highest luminescent efficiency. An inert epitaxial shell layer of NaYF4 grown onto the core of the NaYF4:Er(3+) 10% nanoparticle increased its upconversion emission intensity fivefold due to suppression of surface-related quenching mechanisms, yielding the absolute upconversion efficiency to be as high as ∼3.9±0.3% under an excitation density of 18  W/cm(2). The dependence of the intensity of upconversion emission peaks on laser excitation density in the core/shell nanoparticle displayed "saturation effects" at low excitation density in the range of 1.5-18  W/cm(2), which again demonstrates high upconversion efficiency.