Enhancement of organic solar cells efficiency with acetic acid modulated poly(3,4-ethylenedioxythiophene)
Abstract:
Bulk-heterojunction organic solar cells (OSCs) based on poly(3-hexylthiophene) as a donor material and (6.6) phenyl-C61-butyric acid methyl ester as an acceptor material were investigated using a poly(3,4-ethylenedioxythiophene) poly(styrenesulfonate) (PEDOT:PSS) buffer layer that was modulated with acetic acid. The 1.71 x 10(-1) omega x cm resistivity of the pristine PEDOT:PSS film decreased to 2.29 x 10(-2) omega x cm when acetic acid was applied. This modified PEDOT:PSS buffer layer improved the power conversion efficiency (PCE) of OSCs by reducing their already low series resistance and contact resistance. The PCE of OSCs in which the PEDOT:PSS buffer layers had been treated with acetic acid was 2.91%, an improvement over the 1.82% PCE for cells with pristine PEDOT:PSS layers. We optimized the ratio of acetic acid and PEDOT:PSS solution for high PCE of OSCs in this manuscript. The value of this modification method for hole transporting layer is clearly demonstrated and be applicable to other organic devices.
More Related Videos
08:29Morphology Control for Fully Printable Organic–Inorganic Bulk-heterojunction Solar Cells Based on a Ti-alkoxide and Semiconducting Polymer
Published on: January 10, 2017
14:37Ambient Method for the Production of an Ionically Gated Carbon Nanotube Common Cathode in Tandem Organic Solar Cells
Published on: November 5, 2014