Effect of ultrasonication on physical properties of mineral trioxide aggregate

To evaluate the effect on physical properties of Mineral Trioxide Aggregate (MTA) of using direct hand compaction during placement and when using hand compaction with indirect ultrasonic activation with different application times.

One hundred acrylic canals were obturated in 3 increments with MTA in sample sizes of 10. One group was obturated by hand with an endodontic plugger and the remainder obturated with indirect ultrasonic application, with times ranging from 2 seconds to 18 seconds per increment. Microhardness values, dye penetration depths, and radiographs of the samples were evaluated.

As ultrasonic application time per increment increased, microhardness values fell significantly (P < 0.001) while dye penetration values increased (P < 0.001). Microhardness of MTA ultrasonicated for 2 seconds was significantly higher than hand compaction (P = 0.03). Most radiographic voids were visible in the hand-compacted group (P < 0.001), which also had higher dye penetration depths than the 2-second ultrasonicated samples. Ultrasonication of MTA for 10-18 seconds resulted in significantly more voids than 2-8 seconds of ultrasonication (P = 0.02).

The use of ultrasonics with MTA improved the compaction and flow of MTA, but excessive ultrasonication adversely affected MTA properties. A time of 2 seconds of ultrasonication per increment presented the best compromise between microhardness values, dye penetration depths, and lack of radiographic voids.