Fracture mechanics analyses of ceramic/veneer interface under mixed-mode loading

Gaoqi Wang1, Song Zhang1, Cuirong Bian2

  • 1Key Laboratory of High Efficiency and Clean Mechanical Manufacture (Ministry of Education), School of Mechanical Engineering, Shandong University, Jinan 250061, PR China.

Journal of the Mechanical Behavior of Biomedical Materials
|August 16, 2014
PubMed

Keywords:
Bi-materialsDental ceramicsFracture criterionInterface toughnessMixed-modedental ceramicsinterface fracturemixed-mode loadingveneer chipping

More Related Videos

Fragility Assessment of Bovine Cortical Bone Using Scratch Tests08:36

Fragility Assessment of Bovine Cortical Bone Using Scratch Tests

Published on: November 30, 2017

9.0K
Imaging of the Microstructural Failure Mechanism in the Human Hip08:43

Imaging of the Microstructural Failure Mechanism in the Human Hip

Published on: September 29, 2023

1.8K

Related Concept Videos

Stress-Strain Diagram - Brittle Materials01:24

Stress-Strain Diagram - Brittle Materials

Brittle materials, including glass, cast iron, and stone, exhibit unique characteristics. They fracture without considerable change in their elongation rate, indicating that their breaking and ultimate strength are equivalent. Such materials also show lower strain levels at the point of rupture. The failure in brittle materials predominantly results from normal stresses, as evidenced by the rupture created along a surface perpendicular to the applied load. These materials do not display...
4.4K
Behavior of Concrete Under Compressive Load01:23

Behavior of Concrete Under Compressive Load

Concrete exhibits specific behaviors under different compressive loads. Understanding this is crucial for understanding its structural integrity. When concrete undergoes uniaxial compression, it tends to develop cracks that run parallel to the direction of the force. These parallel cracks stem from localized tensile stresses that occur perpendicular to the compression direction. Additionally, angled cracks may appear due to the formation of shear planes.
As the concrete specimen fractures under...
939
Fractures: Bone Repair01:27

Fractures: Bone Repair

Treatment for a fracture is based on the type of break, the bone affected, and the patient's age.
Minor fractures with no bone displacement are treated by immobilizing the fractured bone using a cast or splint. However, in the case of fractures with displaced bones, the broken bones are repositioned before immobilization to ensure successful healing without deformation and loss of function. The realignment of fractured bone ends is performed through a process called reduction. If the...
5.8K
Relation between Poisson's ratio, Modulus of Elasticity and Modulus of Rigidity01:15

Relation between Poisson's ratio, Modulus of Elasticity and Modulus of Rigidity

Deformation occurs in axial and transverse directions when an axial load is applied to a slender bar. This deformation impacts the cubic element within the bar, transforming it into either a rectangular parallelepiped or a rhombus, contingent on its orientation. This transformation process induces shearing strain. Axial loading elicits both shearing and normal strains. Applying an axial load instigates equal normal and shearing stresses on elements oriented at a 45° angle to the load axis.
821
Stresses under Combined Loadings01:23

Stresses under Combined Loadings

When analyzing a bent tube with a circular cross-section subjected to multiple forces, it is crucial to determine the stress distribution in order to maintain structural integrity under varied load conditions.
The process begins by slicing the tube at critical points and analyzing the internal forces and stress components at these sections, focusing on the centroid. Normal stresses, generated by axial forces and bending moments, are either compressive or tensile and vary across the section from...
603
Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
1.1K