[Preparation and property study of doxorubicin loaded microspheres]

To prepare doxorubicin-loaded polyvinylalcohol-acrylic acid (PVA-AA) microspheres and evaluate properties of this chemoembolic agent.

PVA-AA microspheres were synthesized by inverse suspension polymerization method and then verified by infrared spectroscopy. drug loading (DL) and entrapment efficiency (EE%) were measured after doxorubicinwas loaded on PVA-AA microspheres. Their morphology and elasticity were investigated by optical microscope, environmental scanning electron microscope and texture analyzer, respectively. T-cell apparatus was used to evaluate the in vitro release behavior of doxorubicin-loaded microspheres.The external carotid of the rabbit was chosen as an embolization site to evaluate the in vivo embolic property of the microspheres.

PVA-AA microspheres, which were transparent spheres,turned into red spheres after doxorubicin loading. DL of the microspheres was (20.56 ± 0.69)g/L and (23.25 ± 0.27) g/L,and EE% was 82.22% ± 2.76% and 93.00% ± 1.06% within 20 min and 6 h, respectively. The in vitro release results showed a significantly delayed release of the drug for 10.32% ± 0.47% after 24 h. The Young's modulus was (178.30 ± 12.33) kPa and (213.29 ± 15.61) kPa for blank microspheres and doxorubicin-loaded microspheres, respectively. Both blank microspheres and doxorubicin-loaded microspheres exhibited good elasticity. In vivo embolization showed that 0.3 mL of microspheres could produce distal embolic efficiency.

The doxorubicin-loaded microspheres are expected to be a promising new chemoembolic agent.