Glass-ionomer (Polyalkenoate) cements. Part 1. Development, setting reaction, structure and types

W M Tay1, E Lynch

  • 1Dental Institute, University of London E1 2AD, England.

Journal of the Irish Dental Association
|June 1, 1989
PubMed

Keywords:
dental cementrestorative dentistrypolyacrylic acidfluoride release

More Related Videos

Roughness Impact of Piezoelectric Dental Scaler on Two Distinct Flowable Composite Filling Materials05:30

Roughness Impact of Piezoelectric Dental Scaler on Two Distinct Flowable Composite Filling Materials

Published on: January 10, 2025

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material07:42

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

Related Concept Videos

Anionic Chain-Growth Polymerization: Overview01:20

Anionic Chain-Growth Polymerization: Overview

The polymerization process that involves carbanion as an intermediate is called anionic polymerization. It is also a type of addition or chain-growth polymerization. Anionic polymerization gets initiated by a strong nucleophile such as an organolithium or a Grignard reagent. The most commonly used initiator for anionic polymerization is butyl lithium. Monomers involved in anionic polymerization must possess a vinyl group bonded to one or two electron-withdrawing groups. For instance,...
Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
Setting Time of Cement01:12

Setting Time of Cement

The setting time of cement refers to the process of cement paste transitioning from a plastic state to a solid state. This process is crucial in construction as it dictates the timeframe for concrete placement, compaction, and finishing. The onset of this solidification is termed the initial set, indicating when the paste becomes unworkable. The final set is when the paste has solidified completely, and further handling or manipulation can no longer affect its shape. The cement strength is...
Types of Cement I01:21

Types of Cement I

Portland cement comes in several types, each with distinct properties and applications based on their chemical composition and hydration characteristics:
Type I (Ordinary Portland Cement) is widely used for general construction where special properties are not required. It has moderate sulfate resistance and heat of hydration.
Type II (Modified Cement) offers moderate resistance to sulfate attack and a lower rate of heat development compared to Type I. It is suitable for structures in...
Types of Cement II01:22

Types of Cement II

Portland blast-furnace cement is made by blending Portland cement clinker with granulated blast-furnace slag, which accounts for 25 to 65 percent of the cement's weight. Despite its similarities to ordinary Portland (Type I) cement in terms of fineness and setting times, its early strength is lower, though it achieves comparable strength later on. It's particularly suited for mass concrete structures and marine environments due to its lower heat of hydration and superior sulfate resistance.
Alkali Aggregate Reaction in Concrete01:26

Alkali Aggregate Reaction in Concrete

The alkali-aggregate reaction in concrete involves natural siliceous minerals in aggregates reacting with alkaline hydroxides derived from cement alkalis. This reaction forms an alkali-silica gel that absorbs water, swells, and increases in volume, which is confined by the surrounding cement paste, creating internal pressures that crack and disrupt the concrete. The extent of expansion and damage can be partly attributed to the alkali-silica reaction's osmotic hydraulic pressure and the...