Key Factors Affecting the Performance of Sb2S3-sensitized Solar Cells During an Sb2S3 Deposition via SbCl3-thiourea Complex Solution-processing
Published on: July 16, 2018
Highly reproducible planar Sb₂S₃-sensitized solar cells based on atomic layer deposition
Dae-Hwan Kim1, Sang-Ju Lee, Mi Sun Park
1Energy Research Division, Daegu Gyeongbuk Institute of Science & Technology, 333, Techno jungang-daero, Hyeonpung-myeon, Dalseong-gun, Daegu 711-873, Republic of Korea. imromy@khu.ac.kr sjsung@dgist.ac.kr.
Abstract:
A high-quality Sb₂S₃ thin-absorber with controllable thickness was reproducibly formed by atomic layer deposition (ALD) technique. Compared with conventional chemical bath deposition (CBD), the Sb₂S₃ absorber deposited by ALD did not contain oxide or oxygen impurities and showed a very uniform thickness of Sb₂S₃ absorbers formed on a rough surface of dense blocking TiO₂/F-doped SnOv (bl-TiO₂/FTO) substrate. The planar ALD-Sb₂S₃ solar cells comprised of Au/Poly-3-hexylthiophene/ALD-Sb₂S₃/bl-TiO₂/FTO showed significantly improved power conversion efficiency of 5.77% at 1 sun condition and narrow efficiency deviation, whereas the planar CBD-Sb₂S₃ solar cells exhibited 2.17% power conversion efficiency. The high efficiency and good reproducibility of ALD-Sb₂S₃ solar cell devices is attributed to reduced backward recombination because of the inhibition of oxide defects within ALD-Sb₂S₃ absorber and the conformal deposition of very uniform Sb₂S₃ absorbers on the blocking TiO₂ surface by ALD process.