Aging resistance of surface-treated dental zirconia
Masanao Inokoshi1, Kim Vanmeensel2, Fei Zhang2
1KU Leuven BIOMAT, Department of Oral Health Sciences, KU Leuven (University of Leuven) & Dentistry, University Hospitals Leuven, Kapucijnenvoer 7, blok a bus 7001, B-3000 Leuven, Belgium.
Unlabelled:
The influence of surface treatment on the low-temperature degradation (LTD) of tetragonal zirconia polycrystalline (TZP) is still unclear.
Objectives:
The effect of surface treatments on the LTD behavior of zirconia was investigated.
Methods:
Fully-sintered specimens of seven commercial dental zirconia (Aadva, GC; In-CeramYZ, VITA; IPS e.max ZirCAD, Ivoclar Vivadent; LAVA Frame and LAVA Plus, 3M ESPE; NANOZR, Panasonic; ZirTough, Kuraray Noritake) were provided by the manufacturers with specimen dimensions of approximately 10mm×5mm×3mm. For each zirconia grade, samples were kept 'as sintered' (untreated) or were subjected to one of the three surface treatments: rough polished, sandblasted with Al2O3, tribochemical silica sandblasted (n=3/group). The tetragonal to monoclinic transformation was evaluated by X-ray diffraction at several intervals during LTD testing up to 40h in steam in an autoclave (134°C, 2bar).
Results:
The five yttria-stabilized TZP (Y-TZP: Aadva, In-CeramYZ, IPS e.max ZirCAD, LAVA Frame, LAVA Plus) zirconia showed a similar trend in LTD behavior. The Al2O3 sandblasted zirconia showed the highest monoclinic volume fraction. The as sintered (untreated) zirconia degraded faster than the surface-treated zirconia. Although the surface-treated ceria-stabilized TZP/alumina (Ce-TZP/Al2O3: NANOZR) zirconia had a higher initial monoclinic volume fraction compared to the Y-TZP zirconia, it showed a stronger aging resistance. The as sintered (untreated) Y-TZP/alumina (Y-TZP/Al2O3: ZirTough) zirconia showed a strong aging resistance, whereas the surface-treated Y-TZP/Al2O3 zirconia degraded slightly.
Significance:
Surface treatment improved the aging resistance of Y-TZP zirconia. Surface treatment did not affect the LTD behavior of Ce-TZP/Al2O3 zirconia, while surface treatment decreased the aging resistance of Y-TZP/Al2O3 zirconia.
More Related Videos
07:42Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
Published on: December 20, 2024
08:29Multi-material Ceramic-Based Components – Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing (CerAM - T3DP)
Published on: January 7, 2019