Designed fabrication and characterization of three-dimensionally ordered arrays of core-shell magnetic mesoporous
Kaiping Yuan1, Renchao Che, Qi Cao
1Laboratory of Advanced Materials, Department of Chemistry and Shanghai Key Laboratory of Molecular Catalysis and Innovative Materials, State Key Laboratory of Molecular Engineering of Polymers, Department of Materials Sciences, Collaborative Innovation Center of Chemistry for Energy Materials, Fudan University , Shanghai 200433, P. R. China.
Abstract:
A confined interface coassembly coating strategy based on three-dimensional (3-D) ordered macroporous silica as the nanoreactor was demonstrated for the designed fabrication of novel 3-D ordered arrays of core-shell microspheres consisting of Fe3O4 cores and ordered mesoporous carbon shells. The obtained 3-D ordered arrays of Fe3O4@mesoporous carbon materials possess two sets of periodic structures at both mesoscale and submicrometer scale, high surface area of 326 m(2)/g, and large mesopore size of 19 nm. Microwave absorption test reveals that the obtained materials have excellent microwave absorption performances with maximum reflection loss of up to -57 dB at 8 GHz, and large absorption bandwidth (7.3-13.7 GHz, < -10 dB), due to the combination of the large magnetic loss from iron oxides, the strong dielectric loss from carbonaceous shell, and the strong reflection and scattering of electromagnetic waves of the ordered structures of the mesopores and 3-D arrays of core-shell microspheres.