Low Friction CrN_MPP/TiN_DCMS Multilayer Coatings

Transition metal nitrides like CrN and TiN are widely used in automotive applications due to their high hardness and wear resistance. Recently, we showed that a multilayer architecture of CrN and TiN, deposited using the hybrid-high power impulse magnetron sputtering (HIPIMS) and direct current magnetron sputtering (DCMS)-HIPIMS/DCMS deposition technique, results in coatings which indicate not only increased mechanical and tribological properties but also friction coefficients in the range of diamond-like-carbon coatings when tested at RT and ambient air conditions. The modulated pulsed power (MPP) deposition technique was used to replace the HIPIMS powered cathode within this study to allow for a higher deposition rate, which is based on the complex MPP pulse configuration. Our results on MPP/DCMS deposited CrN/TiN multilayer coatings indicate excellent mechanical and tribological properties, comparable to those obtained for HIPIMS/DCMS. Hardness values are around 25 GPa with wear rates in the range of 2 × 10^-16 Nm/m³ and a coefficient of friction around 0.05 when preparing a superlattice structure. The low friction values can directly be correlated to the relative humidity in the ambient air during dry sliding testing. A minimum relative humidity of 13% is necessary to guarantee such low friction values, as confirmed by repeated tests, which are even obtained after vacuum annealing to 700 °C. Our results demonstrate that the co-sputtering of high metal ion sputtering techniques and conventional DC sputtering opens a new field of applications for CrN/TiN coatings as high wear resistance and low friction coatings.