Spectroscopic and photoluminescence characterization of Dy(3+) in Sr0.5Ca0.5TiO3 phosphor

The spectroscopic and photoluminescence characteristics of trivalent dysprosium (Dy(3+))-doped Sr0.5Ca0.5TiO3 phosphor materials synthesized via solid-state reaction method were studied. The X-ray diffraction profile confirmed the orthorhombic perovskite structure of the prepared samples. Judd-Ofelt analysis was carried out to obtain the intensity parameters and predicted radiative properties of Sr0.5Ca0.5TiO3:2wt%Dy(3+). The photoluminescence spectrum of Dy(3+)-doped Sr0.5Ca0.5TiO3 showed three emission peaks at 481, 574 and 638 nm corresponding to (4)F9/2 →(6)H15/2, (4)F9/2 →(6)H13/2 and (4)F9/2 →(6)H11/2 transitions respectively. The variation of luminescence intensity with different excitation wavelengths and Dy(3+) concentrations is discussed. The decay profiles of (4)F9/2 excited levels of Dy(3+) ions show bi-exponential behaviour and also a decrease in average lifetime with increase in Dy(3+) concentration. Yellow to blue luminescence intensity ratio, CIE chromaticity co-ordinates and correlated color temperature were also calculated for different concentrations of Dy(3+)-doped Sr0.5Ca0.5TiO3 phosphor at different λex.