Starch based biodegradable graft copolymer for the preparation of silver nanoparticles

The synthesis and characterization of a novel biodegradable graft copolymer based on partially hydrolyzed polymethylacrylate (PMA) grafted amylopectin (AP) was reported which was developed for the synthesis of silver nanoparticles from silver nitrate solution by facile green technique. The prepared graft copolymer was biodegradable which was shown by fungal growth. Characterization of silver nanoparticles was carried out by UV-VIS spectroscopy (417nm), HR-TEM, SAED and FESEM analysis. The TEM findings revealed that the silver nanoparticles are crystalline and globular shaped with average particle size ranging from 11 to 15nm. The synthesized silver nanoparticles exhibit excellent antibacterial sensitivity towards both Gram negative and Gram positive bacteria namely Vibrio parahaemolyticus (ATCC-17802) and Bacillus cereus (ATCC-14579) respectively and were also shown a good catalytic activity towards 4-nitrophenol reduction.