Development of novel tricalcium silicate-based endodontic cements with sintered radiopacifier phase

M Xuereb1, F Sorrentino2, D Damidot3,4

  • 1Department of Restorative Dentistry, Faculty of Dental Surgery, Mater Dei Hospital, University of Malta Medical School, Msida, MSD 2090, Malta.

Clinical Oral Investigations
|September 2, 2015
PubMed
Abstract

Keywords:
Bismuth oxideCharacterizationEndodontic cementsHydrationRadiopacifiersSintered radiopacifiersTricalcium silicate cement

More Related Videos

Ceramic Omnidirectional Bioprinting in Cell-Laden Suspensions for the Generation of Bone Analogs10:19

Ceramic Omnidirectional Bioprinting in Cell-Laden Suspensions for the Generation of Bone Analogs

Published on: August 8, 2022

2.5K
Using Baseplating and a Miniscope Preanchored with an Objective Lens for Calcium Transient Research in Mice06:23

Using Baseplating and a Miniscope Preanchored with an Objective Lens for Calcium Transient Research in Mice

Published on: June 5, 2021

4.4K

Related Concept Videos

Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
1.6K
Strength and Heat of Hydration01:29

Strength and Heat of Hydration

The hydration of cement is an exothermic reaction in which heat is generated as cement hydrates. This heat of hydration is critical to cement's strength development. The rate at which this heat is generated affects the temperature rise, with a majority of the heat being released early in the hydration process, half within the first three days, and about 75% within the first week.
The heat of hydration for each cement compound is significant; for instance, tricalcium aluminate (C3A) and...
855
Types of Cement I01:21

Types of Cement I

Portland cement comes in several types, each with distinct properties and applications based on their chemical composition and hydration characteristics:
Type I (Ordinary Portland Cement) is widely used for general construction where special properties are not required. It has moderate sulfate resistance and heat of hydration.
Type II (Modified Cement) offers moderate resistance to sulfate attack and a lower rate of heat development compared to Type I. It is suitable for structures in...
484
Portland Cement01:21

Portland Cement

Portland cement is the essential binding ingredient in concrete, made from finely ground materials including lime, iron, silica, and alumina. Lime is derived primarily from limestone, marble, marl, seashells, and clays, which also supply iron and alumina, while silica is sourced from sand, chalk, and bauxite. Contemporary manufacturing of Portland cement is a significant source of carbon dioxide emissions, prompting research into reducing its content in concrete through alternative...
1.4K
Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is...
556
Setting Time of Cement01:12

Setting Time of Cement

The setting time of cement refers to the process of cement paste transitioning from a plastic state to a solid state. This process is crucial in construction as it dictates the timeframe for concrete placement, compaction, and finishing. The onset of this solidification is termed the initial set, indicating when the paste becomes unworkable. The final set is when the paste has solidified completely, and further handling or manipulation can no longer affect its shape. The cement strength is...
970