Low Pressure Vapor-assisted Solution Process for Tunable Band Gap Pinhole-free Methylammonium Lead Halide Perovskite Films
Published on: September 8, 2017
Ultrasensitive solution-processed broad-band photodetectors using CH₃NH₃PbI₃ perovskite hybrids and PbS quantum dots
Chang Liu1, Kai Wang, Pengcheng Du
1Department of Polymer Engineering, College of Polymer Science and Polymer Engineering, University of Akron, Akron, OH 44325, USA. xgong@uakron.edu.
Abstract:
Sensing from ultraviolet-visible to infrared is critical for both scientific and industrial applications. In this work, we demonstrate solution-processed ultrasensitive broad-band photodetectors (PDs) utilizing organolead halide perovskite materials (CH3NH3PbI3) and PbS quantum dots (QDs) as light harvesters. Through passivating the structural defects on the surface of PbS QDs with diminutive molecular-scaled CH3NH3PbI3, both trap states in the bandgap of PbS QDs for charge carrier recombination and the leakage currents occurring at the defect sites are significantly reduced. In addition, CH3NH3PbI3 itself is an excellent light harvester in photovoltaics, which contributes a great photoresponse in the ultraviolet-visible region. Consequently, operated at room temperature, the resultant PDs show a spectral response from 375 nm to 1100 nm, with high responsivities over 300 mA W(-1) and 130 mA W(-1), high detectivities exceeding 10(13) Jones (1 Jones = 1 cm Hz(1/2) W(-1)) and 5 × 10(12) Jones in the visible and near infrared regions, respectively. These device performance parameters are comparable to those from pristine inorganic counterparts. Thus, our results offer a facile and promising route for advancing the performance of broad-band PDs.