Viscoelastic Properties of Poly[(butylene succinate)-co-adipate] Nanocomposites

Shaeel A Al-Thabaiti, Suprakas Sinha Ray, Sulaiman Nassir Basahell

    Journal of Nanoscience and Nanotechnology
    |September 29, 2015
    PubMed

    More Related Videos

    Synthesis of Thermogelling PolyN-isopropylacrylamide-graft-chondroitin Sulfate Composites with Alginate Microparticles for Tissue Engineering12:22

    Synthesis of Thermogelling PolyN-isopropylacrylamide-graft-chondroitin Sulfate Composites with Alginate Microparticles for Tissue Engineering

    Published on: October 26, 2016

    12.6K
    Characterizing Dissipative Elastic Metamaterials Produced by Additive Manufacturing09:39

    Characterizing Dissipative Elastic Metamaterials Produced by Additive Manufacturing

    Published on: June 28, 2024

    1.8K

    Related Concept Videos

    Polymers: Molecular Weight Distribution01:10

    Polymers: Molecular Weight Distribution

    For any given polymer, the weight average molecular weight (Mw) is higher than, if not equal to, the number average molecular weight (Mn). The only situation in which the weight average molecular weight and the number average molecular weight are equal is when a polymer consists only of chains with equal molecular weight. However, this never happens in a synthetic polymer, since it is difficult to control the polymerization process up to a molecular level with accuracy to a hundred percent.
    5.2K
    Molecular Weight of Step-Growth Polymers01:08

    Molecular Weight of Step-Growth Polymers

    Step growth polymerization involves bi or multifunctional monomers. Bifunctional monomers react to form linear step growth polymers, whereas multifunctional monomers react to form non-linear or branched polymers.
    As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
    The extent of the...
    3.0K
    Olefin Metathesis Polymerization: Acyclic Diene Metathesis (ADMET)00:53

    Olefin Metathesis Polymerization: Acyclic Diene Metathesis (ADMET)

    Acyclic diene metathesis polymerization or ADMET polymerization involves cross-metathesis of terminal dienes, such as 1,8-nonadiene, to give linear unsaturated polymer and ethylene. As ADMET is a reversible process, the formed ethylene gas must be removed from the reaction mixture to complete the polymerization process.
    Similar to cross-metathesis, ADMET also involves the formation of metallacyclobutane intermediate by [2+2] cycloaddition of one of the double bonds of a terminal diene with...
    2.3K
    Characteristics and Nomenclature of Copolymers01:24

    Characteristics and Nomenclature of Copolymers

    Copolymers are the products obtained from the polymerization of multiple monomer species. So, in a polymer chain itself, there can be multiple repeating units that come from different monomers. The process of synthesizing a polymer from different monomer species is called copolymerization. When two monomers are involved, the polymer is known as a bipolymer. Polymers with three and four monomers are termed terpolymers and quaterpolymers, respectively. Figure 1 depicts the copolymerization of...
    3.6K
    Types of Step-Growth Polymers: Polyesters01:20

    Types of Step-Growth Polymers: Polyesters

    The introduction of polyesters has brought major development to the textile industry. The wrinkle-free behavior of polyester blends has eliminated the need for starching and ironing clothes.
    Polyesters are commonly prepared from terephthalic acid and ethylene glycol; the crude product is known as poly(ethylene terephthalate) or PET. However, polyesters are synthesized industrially by transesterification of dimethyl terephthalate with ethylene glycol at 150 °C. The two reactants and the polymer...
    2.7K
    Polymer Classification: Stereospecificity01:26

    Polymer Classification: Stereospecificity

    Polymerization generates chiral centers along the entire backbone of a polymer chain. Accordingly, the stereochemistry of the substituent group has a significant effect on polymer properties. Polymers formed from monosubstituted alkene monomers feature chiral carbons at every alternate position in the polymer backbone. Relative to the predominant orientation of substituents at the adjacent chiral carbons, the polymer can exist in three different configurations: isotactic, syndiotactic, and...
    3.4K