Formulation of Diblock Polymeric Nanoparticles through Nanoprecipitation Technique
Published on: September 20, 2011
Formation and Characterization of Beclomethasone Dipropionate Nanoparticles Using Rapid Expansion of Supercritical
Mohsen Hosseinpour1, Alireza Vatanara2, Reza Zarghami1
1Pharmaceutical Engineering Laboratory, Multiphase Processes Department, School of Chemical Engineering, University of Tehran, Tehran, Iran.
Purpose:
Particle size of Beclometasone Dipropionate (BDP) was reduced by the rapid expansion of supercritical solution (RESS) process, using CO2 as supercritical solvent. Also, the effect of RESS parameters such as extraction pressure, pre-expansion temperature, and weight fraction of co-solvent on the size and distribution of BDP particles were investigated.
Methods:
The effects of extraction pressure (200-260 bar), pre-expansion temperature (70-110 °C) and weight fraction of menthol as a co-solvent on mean particle size (MPS) of BDP were investigated by design of experiment (DOE). Particles were characterized using Scanning Electron Microscopy (SEM) and Dynamic Light Scattering (DLS).
Results:
The average sizes of precipitated BDP were between 64.1 and 294 nm. Analysis of variance (ANOVA) showed that extraction pressure was the most significant parameter and a higher extraction pressure caused production of smaller particles. Also, it was found that higher temperature and weight fraction of co-solvent increased the MPS. The interaction effects of extraction pressure-pre-expansion temperature and pre-expansion temperature-co-solvent ratio were significant through the analysis of variance. It was observed that the MPS of precipitated particles was mostly influenced by pressure.
Conclusion:
The smallest MPS of BDP obtained from the RESS process was 65 nm that revealed a significant size reduction from its original MPS of 9 μm. Moreover, a slight change was observed for precipitated particles of BDP into spherical form while the original particles were irregular in shape. RESS process showed as a promising method for production of BDP nanoparticles that may results in improvement of drug's physicochemical properties.
More Related Videos
09:34Uptake of New Lipid-coated Nanoparticles Containing Falcarindiol by Human Mesenchymal Stem Cells
Published on: February 9, 2019
06:57Rapid, Scalable Assembly and Loading of Bioactive Proteins and Immunostimulants into Diverse Synthetic Nanocarriers Via Flash Nanoprecipitation
Published on: August 11, 2018