Improved Transversal Relaxivity for Highly Crystalline Nanoparticles of Pure γ-Fe2O3 Phase

Pure and highly crystalline γ-Fe2O3 nanocrystals (NCs) are obtained when hydrolysis and oxidation of a Fe(II) organometallic precursor are performed in successive steps. Their synthesis in pure alkylamine leads to NCs of about 6 nm. In aqueous solutions of poly(vinyl)pyrrolidone, such pristine NCs form aggregates of about 150 nm that exhibit a high transversal relaxivity (r2 =466 mM(-1) s(-1)) about four times higher than that of a commercial Feridex magnetic resonance imaging (MRI) contrast agent. Consequently, they provide a significant decrease in the NMR signal at very short echo time (8 ms), which is of paramount importance in clinical practice because of the reduced duration of MRI measurements.