Preparation and Characterization of Ophthalmic Lens Materials Containing Titanium Silicon Oxide and Silver...

Hydrogel ophthalmic lenses containing fluorine-substituted aniline group, titanium silicon oxide nartoparticles, and silver nanoparticles were copolymerized, and the physical and optical properties of the hydrogel lenses were measured. To produce the hydrophilic ophthalmic lenses, the additives were added to the mixture containing HEMA, NVP, MA, EGDMA, and AIBN. The cast mold method was used for the manufacture of the hydrogel ophthalmic lenses, and the produced lenses were completely soaked in a 0.9% NaCl normal saline solution for 24 hours for hydration. The physical properties of the produced macromolecule showed that the water content was 32.5-37.6%, the refractive index was 1.450-1.464, the UV-B transmittance was 0.5-35.2%, and the contact angle was between 56 and 69°. Also, the addition of aniline, titanium silicon oxide, and silver nanoparticles allowed the ophthalmic lenses to block UV. These results show that the produced macromolecule can be used as hydrophilic lenses for ophthalmologic purposes that can block UV.